The electroplating process consists of two main steps: (i) the mass transport of chromium ions through the electrolyte to the surface of the electrode, and (ii) the reduction of chromium ions at the cathode through chemical reactions. c The fundamental equations needed to model the system are: 2.1 Conservation Balances n
Chromium electroplating requires constant control of the plating bath temperature, current density, plating time, and bath composition. Hexavalent chromium plating baths are the most widely used baths to deposit chromium on metal. Hexavalent chromium baths are composed of chromic acid, sulfuric acid, and water.
Chromium plating is traditionally made from a solution of chromic acid (CrO3 which forms H 2 CrO 4 after dissolving in water) and sulfuric acid (H 2 SO 4) using insoluble anodes. The chromium is reduced to metal from the hexavalent state due to the catalytic effect of sulfate ions.
Armelle M. Vardelle. Electroplated hard chromium (EHC) is widely coated onto parts to provide resistance to corrosion, wear and impact. The electroplating process, however, has significant...
13 Σεπ 2024 · Hexavalent chromium, one of the common chrome plating materials, is mainly derived from chromic acid (CrO3). When being dissolved in water, the chromic acid (CrO3) forms H2CrO4 after adding sulfuric acid (H2SO4).
3.1 Influence of bathparameters on the deposition conditions. the plating range of bright and hard chromium deposits depends on the current density and temperature. outside this plating range the chromium deposit is grey, dull and brittle or milky dull and soft.
Electroplating is a chemical or electrochemical process of surface treatment. A metallic layer is deposited on the base material. Common plating metals include: cadmium, chromium, copper, gold, nickel, silver and their alloys. This information bulletin focuses on chrome plating.