The observed XRD peaks and corresponding planes of TiO 2 in PT1, PT2, and PT3, when compared with standard planes (h k l) of TiO 2 , showed good matching, confirming the presence of...
- Login
The observed XRD peaks and corresponding planes of TiO 2 in...
- Help Center
© 2008-2024 ResearchGate GmbH. All rights reserved. Terms;...
- Login
N2 adsorption–desorption isotherms revealed a mesoporous structure for all samples (AC, TiO2@AC-2, and TiO2@AC-10) with hysteresis loops, indicating pores ranging from 2 nm to 50 nm in...
This Calculator can determine crystallite or grain size by using XRD graph. Peak position and FWHM values are needed. Peak Position (2θ) FWHM (2θ) X-Ray Wavelength.
The XRD analysis of the prepared sample of TiO 2 nanoparticles was done using a Bruker make diffractometer, Cu-Kα X-rays of wavelength (λ)=1.5406 Å and data was taken for the 2 θ range of 10° to 70° with a step of 0.1972°.
23 Ιουλ 2019 · X-ray diffraction (XRD) patterns for samples of nanoparticles having different sizes and shapes can look different, and careful analysis of the XRD data can provide useful information and also help correlate microscopic observations with the bulk sample.
1 Ιουλ 2013 · Morphology index (MI) derived from FWHM of XRD data explains the interrelationship of particle size and specific surface area. It is observed that MI has direct relationship with particle size...
29 Σεπ 2009 · This package creates a simulated XRD pattern from a single crystal metal or a binary metal alloy. Base inputs are the cubic structure (SC, FCC, or BCC), lattice parameter, alloy composition, and x-ray wavelength.