  1. The XRD analysis of the prepared sample of TiO 2 nanoparticles was done using a Bruker make diffractometer, Cu-Kα X-rays of wavelength (λ)=1.5406 Å and data was taken for the 2 θ range of 10° to 70° with a step of 0.1972°.

  2. 1 Ιουλ 2013 · Morphology index (MI) derived from FWHM of XRD data explains the interrelationship of particle size and specific surface area. It is observed that MI has direct relationship with particle size...

  3. TEM images show that the grain size of TiO2 micropowders and TiO2 nanopowders are 0.3-0.7 μm and 10 nm, respectively. The selected-area electron diffraction patterns of TiO2 nanopowders in rutile and anatase phases are consistent with XRD results. Key words: TiO2, anatase, rutile, micro and nanopowders, TEM, XRD.

  4. 23 Ιουλ 2019 · Analysis of a sample by powder XRD provides important information that is complementary to various microscopic and spectroscopic methods, such as phase identification, sample purity, crystallite size, and, in some cases, morphology.

  5. XRD results show the formation of highly crystalline titania nanoparticles. It was found that below 400°C anatase phase dominates while annealing at high temperature results in conversion of anatase to rutile phase.

  6. 15 Ιουν 2024 · This study presents a thorough spectroscopic analysis of TiO2-Pt systems under LED irradiation, with a focus on elucidating the photodeposition process of Pt nanoparticles onto TiO2...

  7. X-ray diraction (XRD) is an indispensable tool for characterising thin lms of electroceramic materials. For the beginner, however, it can be a daunting technique at rst due to the number of operation modes and measurements types, as well as the interpretation of the resultant patterns and scans.